- 密度 [g/cm3]: 1.43
- 成型收缩率 [%]: 0.013
- 缺口冲击强度: 1.5
- 弯曲模量 [MPa]: 3.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Filler Content | 5.0 % | 5.0 % | |||
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 3.20 mm | 0.013 in/in @Thickness 0.126 in | Transverse | ||
| 0.014 cm/cm @Thickness 3.20 mm | 0.014 in/in @Thickness 0.126 in | Flow | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | ASTM D638 | ||
| 62.0 MPa @Temperature 23.0 °C | 8990 psi @Temperature 73.4 °F | ISO 527 | |||
| Elongation at Break | 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ASTM D638 | ||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | ISO 527 | |||
| Tensile Modulus | 3.40 GPa @Temperature 23.0 °C | 493 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Modulus | 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | ISO 178 | ||
| 3.20 GPa @Temperature 23.0 °C | 464 ksi @Temperature 73.4 °F | ASTM D790 | |||
| Izod Impact, Notched | 1.50 J/cm @Temperature 23.0 °C | 2.81 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.900 J/cm² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.800 mm | 266 °F @Thickness 0.0315 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | Optimum | |||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | optimum | ||
| 30.0 - 130 °C | 86.0 - 266 °F | ||||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass fiber reinforcement | ||||
| Generic | PBT | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT-IGF5FR(17)< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PBT | ||||
| Product Category | Flame Retardant Resins | ||||
| Glass Reinforced Resins | |||||
| Toughened Resins | |||||
| UV Resistant/Weatherable Resins | |||||
| Resin Identification | PBT-IGF5FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||