- 密度 [g/cm3]: 1.54
- 缺口冲击强度: 0.75
- 拉伸强度 [MPa]: 130.0
- 断裂伸长率 [%]: 160
- 弯曲模量 [MPa]: 8.20
- 硬度: 115.0
- 热变形温度 [℃]: 202.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |