- 密度 [g/cm3]: 1.36
- 缺口冲击强度: 0.9
- 拉伸强度 [MPa]: 97.0
- 断裂伸长率 [%]: 130
- 弯曲模量 [MPa]: 5.80
- 硬度: 110.0
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 130 MPa | 18900 psi | ASTM D790 |
| Flexural Modulus | 5.80 GPa | 841 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |