- 密度 [g/cm3]: 1.08
- 缺口冲击强度: 1.8
- 拉伸强度 [MPa]: 48.0
- 断裂伸长率 [%]: 90.0
- 弯曲模量 [MPa]: 3.20
- 硬度: 105.0
- 热变形温度 [℃]: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 210 - 250 °C | 410 - 482 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |