- 熔体流动速率 [g/10min]: 30.0
- 弯曲模量 [MPa]: 0.179
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Moisture Absorption | 0.300 % @Time 86400 sec | 0.300 % @Time 24.0 hour | ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ISO 294-4 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C | 30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ISO 868 |
| Tensile Strength | 32.4 MPa | 4690 psi | ISO 527 |
| Elongation at Break | 487 % | 487 % | ISO 527 |
| Tensile Modulus | 0.511 GPa | 74.1 ksi | ISO 527 |
| Flexural Modulus | 0.179 GPa | 26.0 ksi | ISO 178 |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.31e+13 ohm-cm | 6.31e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 2.78e+15 ohm | 2.78e+15 ohm | IEC 60093 |
| Dielectric Strength | 17.18 kV/mm @Thickness 2.00 mm | 436.4 kV/in @Thickness 0.0787 in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 212 °C | 414 °F | ISO 3146C |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | |
| Front Barrel Temperature | 230 - 260 °C | 446 - 500 °F | |
| Nozzle Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Injection Pressure | 30.0 - 100 MPa @Time 2.00 - 10.0 sec | 4350 - 14500 psi @Time 0.000556 - 0.00278 hour | |
| Hold Pressure | 5.00 - 40.0 MPa @Time 10.0 - 30.0 sec | 725 - 5800 psi @Time 0.00278 - 0.00833 hour | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |