- 缺口冲击强度: 0.53
- 弯曲模量 [MPa]: 17.9
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.020 - 0.060 cm/cm @Thickness 3.18 mm | 0.020 - 0.060 in/in @Thickness 0.125 in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Thickness 3.18 mm | 0.011 - 0.013 in/in @Thickness 0.125 in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa | 23900 psi | 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D638 | ||
| Tensile Modulus | 21.9 GPa | 3180 ksi | 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 255 MPa | 37000 psi | 1.3 mm/min; ASTM D790 | ||
| Flexural Modulus | 17.9 GPa | 2600 ksi | 1.3 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Unannealed; ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Electrically Conductive | ||||
| Good Chemical Resistance | |||||
| Good Flow | |||||
| High Heat Resistance | |||||
| High Stiffness | |||||
| Semi Crystalline | |||||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 30% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PBT | ||||
| Generic Name | Polybutylene Terephthalate (PBT) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Uses | Appliance Components | ||||
| Appliances | |||||
| Automotive Applications | |||||
| Consumer Applications | |||||
| Housings | |||||
| Industrial Applications | |||||
| Structural Parts | |||||