- 熔体流动速率 [g/10min]: 6.9
- 密度 [g/cm3]: 1.42
- 缺口冲击强度: 6.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00500 - 0.00700 cm/cm | 0.00500 - 0.00700 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0100 - 0.0120 cm/cm | 0.0100 - 0.0120 in/in | ISO 294-4 |
| Melt Flow | 6.90 g/10 min @Load 2.16 kg, Temperature 250 °C | 6.90 g/10 min @Load 4.76 lb, Temperature 482 °F | (MVR) cm³/10min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 83.0 | 83.0 | ISO 2039-2 |
| Tensile Strength at Break | 79.0 MPa | 11500 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 3.10 % | 3.10 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1mm/min; ISO 527-2/1A |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.30 @Frequency 1.00e+6 Hz | 3.30 @Frequency 1.00e+6 Hz | IEC 60250 |
| Dissipation Factor | 0.0150 @Frequency 1.00e+6 Hz | 0.0150 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 425 V | 425 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ISO 75-1, -2 |
| Vicat Softening Point | 207 °C | 405 °F | B50 (50°C/h 50N); ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL94 |