- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 1.51
- 缺口冲击强度: 0.587
- 弯曲模量 [MPa]: 8.00
- 热变形温度 [℃]: 209.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 | ||
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 | ||
| Water Absorption | <= 0.100 % | <= 0.100 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00400 cm/cm | 0.00300 - 0.00400 in/in | ASTM D955 | ||
| 0.00300 - 0.00600 cm/cm | 0.00300 - 0.00600 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.00980 cm/cm | 0.00980 in/in | ISO 294-4 | ||
| Melt Flow | 12.0 - 30.0 g/10 min | 12.0 - 30.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5mm/min; ISO 527-2/1A | ||
| 86.2 MPa | 12500 psi | ASTM D638 | |||
| Elongation at Break | 2.10 % | 2.10 % | 5mm/min; ISO 527-2/1A | ||
| 3.00 % @Temperature 22.8 °C | 3.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 8.00 GPa | 1160 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 | ||
| 140 MPa | 20300 psi | ISO 178 | |||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 | ||
| 6.89 GPa @Temperature 22.8 °C | 1000 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.20 kJ/m² | 2.95 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 19.0 µm/m-°C | 10.6 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 209 °C | 408 °F | ISO 75-1, -2 | ||
| 212 °C | 414 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 172 °C | 342 °F | ISO 75-1, -2 | ||
| 175 °C | 347 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |||
| Zone 2 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 3 | 235 - 255 °C | 455 - 491 °F | |||
| Zone 4 | 240 - 265 °C | 464 - 509 °F | |||
| Die Temperature | 240 - 265 °C | 464 - 509 °F | |||
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | |||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 82.0 °C | 180 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 265 °C | 482 - 509 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||