- 密度 [g/cm3]: 1.25
- 拉伸强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 1.40
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0170 - 0.0220 cm/cm | 0.0170 - 0.0220 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.5 MPa | 5000 psi | ASTM D638 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 180 % | 180 % | 50mm/min; ISO 527-2/1A |
| 180 % @Temperature 22.8 °C | 180 % @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Yield | 6.00 % | 6.00 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 1.50 GPa | 218 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 45.0 MPa | 6530 psi | ISO 178 |
| 49.0 MPa | 7100 psi | ASTM D790 | |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| 1.52 GPa @Temperature 22.8 °C | 220 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/1A |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |