- 缺口冲击强度: 0.908
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.175 mm | 0.0010 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 93.1 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| Flexural Strength | 157 MPa | 22700 psi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |