- 密度 [g/cm3]: 1.42
- 缺口冲击强度: 4.0
- 弯曲强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 5.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ISO Data | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK5830 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||