- 密度 [g/cm3]: 1.68
- 缺口冲击强度: 0.9
- 弯曲强度 [MPa]: 130.0
- 弯曲模量 [MPa]: 9.70
- 硬度: 118.0
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | ||
| Viscosity Measurement | 0.49 | 0.49 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 11.1 GPa | 1610 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 210 MPa | 30500 psi | ASTM Test | ||
| 85.0 MPa @Temperature 120 °C | 12300 psi @Temperature 248 °F | ASTM Test | |||
| 275 MPa @Temperature -40.0 °C | 39900 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM Test | ||
| 2.97 GPa @Temperature 120 °C | 431 ksi @Temperature 248 °F | ASTM Test | |||
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.17 mm | 1.69 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 13.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | ASTM Test | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| 220 °C | 428 °F | ASTM Test | |||
| Flammability, UL94 | V-0 @Thickness 0.300 mm | V-0 @Thickness 0.0118 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| 5VA @Thickness 0.800 mm | 5VA @Thickness 0.0315 in | ||||
| Oxygen Index | 36 % | 36 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Injection Velocity | 115 mm/sec | 4.53 in/sec | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| UL.UL-C | Yes | ||||