- 熔体流动速率 [g/10min]: 6.0
- 吸水率 [%]: 0.15
- 缺口冲击强度: 6.41
- 拉伸强度 [MPa]: 53.8
- 弯曲模量 [MPa]: 2.18
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°F; ASTM D570 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | 73°F; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 6.0 g/10 min @Load 8.38 lb, Temperature 446 °F | Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | chs 2 in/min; ASTM D638 |
| Elongation at Break | 27 % | 27 % | ASTM D638 |
| Flexural Modulus | 2.18 GPa | 316 ksi | Tangent (chs speed 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | 0.125 in bar, Unannealed/Conditioned 48 hours; ASTM D648 |