- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 51.0
- 断裂伸长率 [%]: 73.0
- 透光率 [%]: 67.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 0.490 g/m²/day | 0.0316 g/100 in²/day | ASTM F372 |
| Oxygen Transmission | 23.0 cc-mm/m²-24hr-atm | 58.4 cc-mil/100 in²-24hr-atm | ASTM D3985 |
| Viscosity Measurement | 0.70 | 0.70 | Inherent; EMN-A-AC-G-V-1 |
| Thickness | 254 microns | 10.0 mil | ASTM D374 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 184 % | 184 % | ASTM D638 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C | 0.749 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| 0.650 J/cm @Temperature 23.0 °C | 1.22 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D4812 | |
| Puncture Energy | 24.0 J @Thickness 3.20 mm, Temperature -40.0 °C | 17.7 ft-lb @Thickness 0.126 in, Temperature -40.0 °F | max load; ASTM D3763 |
| 33.0 J @Thickness 3.20 mm, Temperature 23.0 °C | 24.3 ft-lb @Thickness 0.126 in, Temperature 73.4 °F | max load; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 74.0 °C | 165 °F | 1kg load; ASTM D1525 |
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.70 % | 0.70 % | ASTM D1003 |
| Gloss | 166 % | 166 % | at 60°; ASTM D2457 |
| Transmission, Visible | 67 % | 67 % | Transparency; ASTM D1746 |
| 89 % | 89 % | Regular Transmittance; ASTM D1003 | |
| 92 % | 92 % | Total Transmittance; ASTM D1003 | |