- 密度 [g/cm3]: 1.16
- 拉伸强度 [MPa]: 46.0
- 热变形温度 [℃]: 102.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.8 % | 4.8 % | |
| Tensile Modulus | 1.54 GPa | 223 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 5.50 J/cm² | 26.2 ft-lb/in² | Partial Break |
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | Partial Break | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 87.0 µm/m-°C @Temperature 20.0 °C | 48.3 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature 20.0 °C | 46.1 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 241 °C | 466 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | |
| Vicat Softening Point | 106 °C | 223 °F | |
| Glass Transition Temp, Tg | 111 °C | 232 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | |