- 密度 [g/cm3]: 1.33
- 拉伸强度 [MPa]: 57.0
- 热变形温度 [℃]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 3.8 % | 3.8 % | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 0.490 J/cm² | 2.33 ft-lb/in² | |
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 77.0 µm/m-°C @Temperature 20.0 °C | 42.8 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 48.0 µm/m-°C @Temperature 20.0 °C | 26.7 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 250 °C | 482 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | |
| Vicat Softening Point | 74.0 °C | 165 °F | |
| Glass Transition Temp, Tg | 77.0 °C | 171 °F | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |