- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.32
- 拉伸强度 [MPa]: 79.3
- 弯曲模量 [MPa]: 2.83
- 硬度: 114.0
- 热变形温度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 |
| Flexural Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 411 ksi | ASTM D790 |
| Compressive Strength | 35.9 MPa | 5200 psi | ASTM D695 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | 40 psi, 50 fpm; ASTM D3702 |
| Coefficient of Friction, Static | 0.19 | 0.19 | ASTM D3702 |
| K (wear) Factor | 423 x 10-8 mm³/N-M | 210 x 10-10 in³-min/ft-lb-hr | 40 psi, 50 fpm; ASTM D3702 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 60 Hz | 3.4 @Frequency 60 Hz | 50% RH; ASTM D150 |
| 3.7 @Frequency 60 Hz | 3.7 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 60 Hz | 0.0020 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.2 µm/m-°C @Temperature 20.0 °C | 39.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.17 J/g-°C | 0.280 BTU/lb-°F | |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | |
| Melting Point | 254 °C | 490 °F | ASTM D2133 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Long Term; ASTM UL746B |
| 160 °C | 320 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |