- 密度 [g/cm3]: 1.58
- 缺口冲击强度: 0.68
- 拉伸强度 [MPa]: 98.0
- 断裂伸长率 [%]: 150
- 弯曲模量 [MPa]: 9.60
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | ASTM D638 |
| Flexural Yield Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 9.60 GPa | 1390 ksi | ASTM D790 |
| Izod Impact, Notched | 0.680 J/cm | 1.27 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |