- 密度 [g/cm3]: 1.56
- 缺口冲击强度: 1.01
- 拉伸强度 [MPa]: 155.0
- 断裂伸长率 [%]: 235
- 弯曲模量 [MPa]: 8.90
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 155 MPa | 22500 psi | ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| Flexural Yield Strength | 235 MPa | 34100 psi | ASTM D790 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D3418 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |