- 缺口冲击强度: 1.08
- 弯曲模量 [MPa]: 17.9
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 g/cc | 1.77 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 188.352 MPa | 27318.2 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 289.4 MPa | 41970 psi | ASTM D790 |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |