- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.08
- 缺口冲击强度: 0.53
- 断裂伸长率 [%]: 153.2
- 弯曲强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 6.61
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0016 cm/cm | 0.0016 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 1.76 % | 1.76 % | ASTM D638 |
| Flexural Yield Strength | 153.2 MPa | 22220 psi | ASTM D790 |
| Flexural Modulus | 6.61 GPa | 959 ksi | ASTM D790 |
| Compressive Yield Strength | 170.3 MPa | 24700 psi | ASTM D695 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.4345e+16 ohm-cm | 5.4345e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 16.9 kV/mm | 429 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.014 @Frequency 1e+6 Hz | 0.014 @Frequency 1e+6 Hz | ASTM D150 |
| Comparative Tracking Index | 225 V | 225 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |