- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.72
- 断裂伸长率 [%]: 214.5
- 弯曲强度 [MPa]: 136.6
- 弯曲模量 [MPa]: 10.76
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 136.6 MPa | 19810 psi | ASTM D638 |
| Elongation at Break | 1.58 % | 1.58 % | ASTM D638 |
| Tensile Modulus | 10.92 GPa | 1584 ksi | ASTM D638 |
| Flexural Yield Strength | 214.5 MPa | 31110 psi | ASTM D790 |
| Flexural Modulus | 10.76 GPa | 1561 ksi | ASTM D790 |
| Compressive Yield Strength | 173.1 MPa | 25110 psi | ASTM D695 |
| Izod Impact, Notched | 0.720 J/cm | 1.35 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.5307e+16 ohm-cm | 3.5307e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.012 @Frequency 1e+6 Hz | 0.012 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 30 sec | 30 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |