- 密度 [g/cm3]: 1.63
- 吸水率 [%]: 0.07
- 缺口冲击强度: 0.54
- 断裂伸长率 [%]: 187.2
- 弯曲强度 [MPa]: 123.9
- 弯曲模量 [MPa]: 8.74
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0024 cm/cm | 0.0024 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 123.9 MPa | 17970 psi | ASTM D638 |
| Elongation at Break | 1.99 % | 1.99 % | ASTM D638 |
| Flexural Yield Strength | 187.2 MPa | 27150 psi | ASTM D790 |
| Flexural Modulus | 8.74 GPa | 1270 ksi | ASTM D790 |
| Compressive Yield Strength | 170.7 MPa | 24760 psi | ASTM D695 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 9.14e+15 ohm-cm | 9.14e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 19.4 kV/mm | 493 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | ASTM D150 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |