- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.06
- 缺口冲击强度: 0.61
- 断裂伸长率 [%]: 155.9
- 弯曲强度 [MPa]: 114.2
- 弯曲模量 [MPa]: 6.99
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 114.2 MPa | 16560 psi | ASTM D638 |
| Elongation at Break | 1.97 % | 1.97 % | ASTM D638 |
| Tensile Modulus | 6.53 GPa | 947 ksi | ASTM D638 |
| Flexural Yield Strength | 155.9 MPa | 22610 psi | ASTM D790 |
| Flexural Modulus | 6.99 GPa | 1010 ksi | ASTM D790 |
| Compressive Yield Strength | 155.8 MPa | 22600 psi | ASTM D695 |
| Izod Impact, Notched | 0.610 J/cm | 1.14 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.695e+16 ohm-cm | 3.695e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 17.2 kV/mm | 437 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.014 @Frequency 1e+6 Hz | 0.014 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Comparative Tracking Index | 225 V | 225 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.47 mm | HB @Thickness 0.0579 in | |