- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.62
- 断裂伸长率 [%]: 199.7
- 弯曲强度 [MPa]: 133.4
- 弯曲模量 [MPa]: 10.58
- 硬度: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0011 cm/cm | 0.0011 in/in | ATM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 19 | 19 | ASTM D785 |
| Tensile Strength, Ultimate | 133.4 MPa | 19350 psi | ASTM D638 |
| Elongation at Break | 1.51 % | 1.51 % | ASTM D638 |
| Tensile Modulus | 10.79 GPa | 1565 ksi | ASTM D638 |
| Flexural Yield Strength | 199.7 MPa | 28960 psi | ASTM D790 |
| Flexural Modulus | 10.58 GPa | 1535 ksi | ASTM D790 |
| Compressive Yield Strength | 161.5 MPa | 23420 psi | ASTM D695 |
| Izod Impact, Notched | 0.620 J/cm | 1.16 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 7.945e+15 ohm-cm | 7.945e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | ASTM D150 |
| Arc Resistance | 70 sec | 70 sec | ASTM D495 |
| Comparative Tracking Index | 200 V | 200 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm | V-0 @Thickness 0.0579 in | |
| Oxygen Index | 31.5 % | 31.5 % | ASTM D2863 |