- 密度 [g/cm3]: 1.25
- 缺口冲击强度: 9.61
- 拉伸强度 [MPa]: 28.3
- 弯曲模量 [MPa]: 1.24
- 热变形温度 [℃]: 60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | ASTM D638 | ||
| Elongation at Break | 350 % | 350 % | ASTM D638 | ||
| Tensile Modulus | 1.10 GPa | 160 ksi | ASTM D638 | ||
| Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790-92 | ||
| Izod Impact, Notched | 9.61 J/cm | 18.0 ft-lb/in | ASTM D256-92 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+9 ohm-cm | 2.00e+9 ohm-cm | 50% RH; ASTM D257 | ||
| Surface Resistance | 8.00e+8 ohm | 8.00e+8 ohm | ESD S11.11; 12 % R.H. | ||
| Surface Resistivity per Square | 2.00e+9 ohm | 2.00e+9 ohm | ASTM D257 | ||
| Static Decay | 0.010 sec | 0.010 sec | FTMS-101C; 12% R.H., (+5000 V to 50 V) | ||
| 0.010 sec | 0.010 sec | FTMS-101C; 12% R.H., (-5000 V to -50 V) | |||
| 0.10 sec | 0.10 sec | Charged Plate Monitor; 50% R.H. MD, (+1000 V to 10 V) | |||
| Tribocharge | 10 V | 10 V | Nitrile Glove - BFG Test Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Color | Light Blue | ||||