- 密度 [g/cm3]: 1.38
- 缺口冲击强度: 10.0
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm | 0.0015 - 0.0030 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 252 °C | 486 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |