- 熔体流动速率 [g/10min]: 15.0
- 缺口冲击强度: 2.94
- 断裂伸长率 [%]: 17.8
- 弯曲强度 [MPa]: 21.6
- 弯曲模量 [MPa]: 0.2858
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C | 15 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 21.6 MPa | 3130 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Yield Strength | 17.8 MPa | 2590 psi | ASTM D790 |
| Flexural Modulus | 0.2858 GPa | 41.45 ksi | ASTM D790 |
| Izod Impact, Notched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 90.0 °C | 194 °F | ASTM D3418 |
| Softening Point | 79.0 °C | 174 °F | ASTM D1525 |