- 密度 [g/cm3]: 1.55
- 缺口冲击强度: 0.85
- 断裂伸长率 [%]: 190
- 弯曲强度 [MPa]: 135.0
- 弯曲模量 [MPa]: 9.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0070 cm/cm | 0.0060 - 0.0070 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527-93 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-93 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ISO 178-93 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | ISO 178-93 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 250 °C | 482 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-93 |