- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 5.5
- 弯曲模量 [MPa]: 5.80
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | ||
| Filler Content | 15 % | 15 % | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 6.50 GPa @Temperature 23.0 °C | 943 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 5.80 GPa @Temperature 23.0 °C | 841 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.550 J/cm² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 227 °C | 441 °F | 10°C/min; ISO 11357-1/-3 | ||
| 260 °C | 500 °F | Optimum | |||
| 250 - 270 °C | 482 - 518 °F | ||||
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |||
| 100 °C | 212 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Filler | Glass Reinforced | ||||
| Forms | Pellets | ||||
| Generic | Polytrimethylene Terephthalate (PTT) | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PTT-GF15< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Food Contact Resins | ||||
| Glass Reinforced Resins | |||||
| Renewably Sourced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PTT-GF15 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Food Applications, Non-specific | ||||