  4. DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)

DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)

DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT) 物性表: DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)物性表及特性介绍,DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)注塑参数详情,如需DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.4
  • 吸水率 [%]: 0.08
  • 弯曲模量 [MPa]: 5.80
  • 热变形温度 [℃]: 223.0
 
Physical PropertiesMetricEnglishComments
Density 1.40 g/cc0.0506 lb/in³ISO 1183
Filler Content 15 %15 %
Water Absorption 0.080 %
@Temperature 23.0 °C		0.080 %
@Temperature 73.4 °F		Immersion 24h; ISO 62, Similar to
Linear Mold Shrinkage, Flow  0.0020 cm/cm
@Thickness 2.00 mm		0.0020 in/in
@Thickness 0.0787 in		Mold 80°C; ISO 294-4
 0.0030 cm/cm
@Thickness 3.00 mm		0.0030 in/in
@Thickness 0.118 in		Mold 80°C; ISO 294-4
 0.0040 cm/cm
@Thickness 4.00 mm		0.0040 in/in
@Thickness 0.157 in		Mold 80°C; ISO 294-4
Linear Mold Shrinkage, Transverse  0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Mold 80°C; ISO 294-4
 0.0070 cm/cm
@Thickness 3.00 mm		0.0070 in/in
@Thickness 0.118 in		Mold 80°C; ISO 294-4
 0.010 cm/cm
@Thickness 4.00 mm		0.010 in/in
@Thickness 0.157 in		Mold 80°C; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 125 MPa
@Temperature 23.0 °C		18100 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  1.984 MPa
@Strain 0.100 %,
Temperature 150 °C		287.8 psi
@Strain 0.100 %,
Temperature 302 °F		ISO 11403-1/-2
 2.26 MPa
@Strain 0.100 %,
Temperature 120 °C		328 psi
@Strain 0.100 %,
Temperature 248 °F		ISO 11403-1/-2
 2.481 MPa
@Strain 0.100 %,
Temperature 100 °C		359.8 psi
@Strain 0.100 %,
Temperature 212 °F		ISO 11403-1/-2
 2.741 MPa
@Strain 0.100 %,
Temperature 80.0 °C		397.5 psi
@Strain 0.100 %,
Temperature 176 °F		ISO 11403-1/-2
 3.453 MPa
@Strain 0.100 %,
Temperature 60.0 °C		500.8 psi
@Strain 0.100 %,
Temperature 140 °F		ISO 11403-1/-2
 3.928 MPa
@Strain 0.200 %,
Temperature 150 °C		569.7 psi
@Strain 0.200 %,
Temperature 302 °F		ISO 11403-1/-2
 4.498 MPa
@Strain 0.200 %,
Temperature 120 °C		652.4 psi
@Strain 0.200 %,
Temperature 248 °F		ISO 11403-1/-2
 4.942 MPa
@Strain 0.200 %,
Temperature 100 °C		716.8 psi
@Strain 0.200 %,
Temperature 212 °F		ISO 11403-1/-2
 5.491 MPa
@Strain 0.200 %,
Temperature 80.0 °C		796.4 psi
@Strain 0.200 %,
Temperature 176 °F		ISO 11403-1/-2
 5.856 MPa
@Strain 0.300 %,
Temperature 150 °C		849.3 psi
@Strain 0.300 %,
Temperature 302 °F		ISO 11403-1/-2
 5.916 MPa
@Strain 0.100 %,
Temperature 40.0 °C		858.0 psi
@Strain 0.100 %,
Temperature 104 °F		ISO 11403-1/-2
 6.20 MPa
@Strain 0.100 %,
Temperature 23.0 °C		899 psi
@Strain 0.100 %,
Temperature 73.4 °F		ISO 11403-1/-2
 6.303 MPa
@Strain 0.100 %,
Temperature 0.000 °C		914.2 psi
@Strain 0.100 %,
Temperature 32.0 °F		ISO 11403-1/-2
 6.77 MPa
@Strain 0.300 %,
Temperature 120 °C		982 psi
@Strain 0.300 %,
Temperature 248 °F		ISO 11403-1/-2
 6.80 MPa
@Strain 0.100 %,
Temperature -40.0 °C		986 psi
@Strain 0.100 %,
Temperature -40.0 °F		ISO 11403-1/-2
 7.149 MPa
@Strain 0.200 %,
Temperature 60.0 °C		1037 psi
@Strain 0.200 %,
Temperature 140 °F		ISO 11403-1/-2
 7.19 MPa
@Strain 0.300 %,
Temperature 100 °C		1040 psi
@Strain 0.300 %,
Temperature 212 °F		ISO 11403-1/-2
 7.213 MPa
@Strain 0.400 %,
Temperature 150 °C		1046 psi
@Strain 0.400 %,
Temperature 302 °F		ISO 11403-1/-2
 7.928 MPa
@Strain 0.300 %,
Temperature 80.0 °C		1150 psi
@Strain 0.300 %,
Temperature 176 °F		ISO 11403-1/-2
 8.659 MPa
@Strain 0.400 %,
Temperature 120 °C		1256 psi
@Strain 0.400 %,
Temperature 248 °F		ISO 11403-1/-2
 9.212 MPa
@Strain 0.500 %,
Temperature 150 °C		1336 psi
@Strain 0.500 %,
Temperature 302 °F		ISO 11403-1/-2
 9.232 MPa
@Strain 0.400 %,
Temperature 100 °C		1339 psi
@Strain 0.400 %,
Temperature 212 °F		ISO 11403-1/-2
 10.247 MPa
@Strain 0.400 %,
Temperature 80.0 °C		1486.2 psi
@Strain 0.400 %,
Temperature 176 °F		ISO 11403-1/-2
 10.512 MPa
@Strain 0.300 %,
Temperature 60.0 °C		1524.6 psi
@Strain 0.300 %,
Temperature 140 °F		ISO 11403-1/-2
 10.886 MPa
@Strain 0.600 %,
Temperature 150 °C		1578.9 psi
@Strain 0.600 %,
Temperature 302 °F		ISO 11403-1/-2
 11.106 MPa
@Strain 0.500 %,
Temperature 120 °C		1610.8 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 11403-1/-2
 11.846 MPa
@Strain 0.200 %,
Temperature 40.0 °C		1718.1 psi
@Strain 0.200 %,
Temperature 104 °F		ISO 11403-1/-2
 12.025 MPa
@Strain 0.500 %,
Temperature 100 °C		1744.1 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 11403-1/-2
 12.2 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1770 psi
@Strain 0.200 %,
Temperature 73.4 °F		ISO 11403-1/-2
 12.375 MPa
@Strain 0.700 %,
Temperature 150 °C		1794.8 psi
@Strain 0.700 %,
Temperature 302 °F		ISO 11403-1/-2
 12.634 MPa
@Strain 0.200 %,
Temperature 0.000 °C		1832.4 psi
@Strain 0.200 %,
Temperature 32.0 °F		ISO 11403-1/-2
 13.115 MPa
@Strain 0.600 %,
Temperature 120 °C		1902.2 psi
@Strain 0.600 %,
Temperature 248 °F		ISO 11403-1/-2
 13.194 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1913.6 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 11403-1/-2
 13.503 MPa
@Strain 0.400 %,
Temperature 60.0 °C		1958.4 psi
@Strain 0.400 %,
Temperature 140 °F		ISO 11403-1/-2
 13.762 MPa
@Strain 0.200 %,
Temperature -40.0 °C		1996.0 psi
@Strain 0.200 %,
Temperature -40.0 °F		ISO 11403-1/-2
 13.829 MPa
@Strain 0.800 %,
Temperature 150 °C		2005.7 psi
@Strain 0.800 %,
Temperature 302 °F		ISO 11403-1/-2
 14.278 MPa
@Strain 0.600 %,
Temperature 100 °C		2070.9 psi
@Strain 0.600 %,
Temperature 212 °F		ISO 11403-1/-2
 14.991 MPa
@Strain 0.700 %,
Temperature 120 °C		2174.3 psi
@Strain 0.700 %,
Temperature 248 °F		ISO 11403-1/-2
 15.22 MPa
@Strain 0.900 %,
Temperature 150 °C		2207 psi
@Strain 0.900 %,
Temperature 302 °F		ISO 11403-1/-2
 15.794 MPa
@Strain 0.600 %,
Temperature 80.0 °C		2290.7 psi
@Strain 0.600 %,
Temperature 176 °F		ISO 11403-1/-2
 16.3 MPa
@Strain 0.700 %,
Temperature 100 °C		2360 psi
@Strain 0.700 %,
Temperature 212 °F		ISO 11403-1/-2
 16.494 MPa
@Strain 1.00 %,
Temperature 150 °C		2392.3 psi
@Strain 1.00 %,
Temperature 302 °F		ISO 11403-1/-2
 16.694 MPa
@Strain 0.800 %,
Temperature 120 °C		2421.3 psi
@Strain 0.800 %,
Temperature 248 °F		ISO 11403-1/-2
 17.519 MPa
@Strain 0.500 %,
Temperature 60.0 °C		2540.9 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 11403-1/-2
 17.738 MPa
@Strain 1.10 %,
Temperature 150 °C		2572.7 psi
@Strain 1.10 %,
Temperature 302 °F		ISO 11403-1/-2
 17.874 MPa
@Strain 0.300 %,
Temperature 40.0 °C		2592.4 psi
@Strain 0.300 %,
Temperature 104 °F		ISO 11403-1/-2
 17.9 MPa
@Strain 0.300 %,
Temperature 23.0 °C		2600 psi
@Strain 0.300 %,
Temperature 73.4 °F		ISO 11403-1/-2
 18.113 MPa
@Strain 0.700 %,
Temperature 80.0 °C		2627.1 psi
@Strain 0.700 %,
Temperature 176 °F		ISO 11403-1/-2
 18.295 MPa
@Strain 0.800 %,
Temperature 100 °C		2653.5 psi
@Strain 0.800 %,
Temperature 212 °F		ISO 11403-1/-2
 18.393 MPa
@Strain 0.900 %,
Temperature 120 °C		2667.7 psi
@Strain 0.900 %,
Temperature 248 °F		ISO 11403-1/-2
 18.44 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2675 psi
@Strain 0.300 %,
Temperature 32.0 °F		ISO 11403-1/-2
 18.885 MPa
@Strain 1.20 %,
Temperature 150 °C		2739.0 psi
@Strain 1.20 %,
Temperature 302 °F		ISO 11403-1/-2
 18.97 MPa
@Strain 0.300 %,
Temperature -40.0 °C		2751 psi
@Strain 0.300 %,
Temperature -40.0 °F		ISO 11403-1/-2
 19.989 MPa
@Strain 1.00 %,
Temperature 120 °C		2899.2 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 11403-1/-2
 20.033 MPa
@Strain 1.30 %,
Temperature 150 °C		2905.5 psi
@Strain 1.30 %,
Temperature 302 °F		ISO 11403-1/-2
 20.196 MPa
@Strain 0.900 %,
Temperature 100 °C		2929.2 psi
@Strain 0.900 %,
Temperature 212 °F		ISO 11403-1/-2
 20.396 MPa
@Strain 0.800 %,
Temperature 80.0 °C		2958.2 psi
@Strain 0.800 %,
Temperature 176 °F		ISO 11403-1/-2
 20.95 MPa
@Strain 0.600 %,
Temperature 60.0 °C		3039 psi
@Strain 0.600 %,
Temperature 140 °F		ISO 11403-1/-2
 21.097 MPa
@Strain 1.40 %,
Temperature 150 °C		3059.9 psi
@Strain 1.40 %,
Temperature 302 °F		ISO 11403-1/-2
 21.504 MPa
@Strain 1.10 %,
Temperature 120 °C		3118.9 psi
@Strain 1.10 %,
Temperature 248 °F		ISO 11403-1/-2
 21.939 MPa
@Strain 1.00 %,
Temperature 100 °C		3182.0 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 11403-1/-2
 22.044 MPa
@Strain 1.50 %,
Temperature 150 °C		3197.2 psi
@Strain 1.50 %,
Temperature 302 °F		ISO 11403-1/-2
 22.541 MPa
@Strain 0.900 %,
Temperature 80.0 °C		3269.3 psi
@Strain 0.900 %,
Temperature 176 °F		ISO 11403-1/-2
 22.987 MPa
@Strain 1.20 %,
Temperature 120 °C		3334.0 psi
@Strain 1.20 %,
Temperature 248 °F		ISO 11403-1/-2
 22.992 MPa
@Strain 1.60 %,
Temperature 150 °C		3334.7 psi
@Strain 1.60 %,
Temperature 302 °F		ISO 11403-1/-2
 23.084 MPa
@Strain 0.400 %,
Temperature 40.0 °C		3348.1 psi
@Strain 0.400 %,
Temperature 104 °F		ISO 11403-1/-2
 23.144 MPa
@Strain 0.400 %,
Temperature 23.0 °C		3356.8 psi
@Strain 0.400 %,
Temperature 73.4 °F		ISO 11403-1/-2
 23.367 MPa
@Strain 0.400 %,
Temperature 0.000 °C		3389.1 psi
@Strain 0.400 %,
Temperature 32.0 °F		ISO 11403-1/-2
 23.679 MPa
@Strain 1.10 %,
Temperature 100 °C		3434.4 psi
@Strain 1.10 %,
Temperature 212 °F		ISO 11403-1/-2
 23.861 MPa
@Strain 1.70 %,
Temperature 150 °C		3460.8 psi
@Strain 1.70 %,
Temperature 302 °F		ISO 11403-1/-2
 24.235 MPa
@Strain 0.700 %,
Temperature 60.0 °C		3515.0 psi
@Strain 0.700 %,
Temperature 140 °F		ISO 11403-1/-2
 24.37 MPa
@Strain 1.30 %,
Temperature 120 °C		3535 psi
@Strain 1.30 %,
Temperature 248 °F		ISO 11403-1/-2
 24.38 MPa
@Strain 0.400 %,
Temperature -40.0 °C		3536 psi
@Strain 0.400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 24.54 MPa
@Strain 1.00 %,
Temperature 80.0 °C		3559 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 11403-1/-2
 24.646 MPa
@Strain 1.80 %,
Temperature 150 °C		3574.6 psi
@Strain 1.80 %,
Temperature 302 °F		ISO 11403-1/-2
 25.266 MPa
@Strain 1.20 %,
Temperature 100 °C		3664.5 psi
@Strain 1.20 %,
Temperature 212 °F		ISO 11403-1/-2
 25.445 MPa
@Strain 1.90 %,
Temperature 150 °C		3690.5 psi
@Strain 1.90 %,
Temperature 302 °F		ISO 11403-1/-2
 25.706 MPa
@Strain 1.40 %,
Temperature 120 °C		3728.3 psi
@Strain 1.40 %,
Temperature 248 °F		ISO 11403-1/-2
 26.154 MPa
@Strain 2.00 %,
Temperature 150 °C		3793.3 psi
@Strain 2.00 %,
Temperature 302 °F		ISO 11403-1/-2
 26.557 MPa
@Strain 1.10 %,
Temperature 80.0 °C		3851.8 psi
@Strain 1.10 %,
Temperature 176 °F		ISO 11403-1/-2
 26.803 MPa
@Strain 1.30 %,
Temperature 100 °C		3887.5 psi
@Strain 1.30 %,
Temperature 212 °F		ISO 11403-1/-2
 26.812 MPa
@Strain 2.10 %,
Temperature 150 °C		3888.8 psi
@Strain 2.10 %,
Temperature 302 °F		ISO 11403-1/-2
 26.921 MPa
@Strain 1.50 %,
Temperature 120 °C		3904.6 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 11403-1/-2
 27.15 MPa
@Strain 2.20 %,
Temperature 150 °C		3938 psi
@Strain 2.20 %,
Temperature 302 °F		ISO 11403-1/-2
 27.337 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3964.9 psi
@Strain 0.800 %,
Temperature 140 °F		ISO 11403-1/-2
 28.18 MPa
@Strain 1.60 %,
Temperature 120 °C		4087 psi
@Strain 1.60 %,
Temperature 248 °F		ISO 11403-1/-2
 28.306 MPa
@Strain 1.40 %,
Temperature 100 °C		4105.4 psi
@Strain 1.40 %,
Temperature 212 °F		ISO 11403-1/-2
 28.439 MPa
@Strain 1.20 %,
Temperature 80.0 °C		4124.7 psi
@Strain 1.20 %,
Temperature 176 °F		ISO 11403-1/-2
 29.325 MPa
@Strain 1.70 %,
Temperature 120 °C		4253.2 psi
@Strain 1.70 %,
Temperature 248 °F		ISO 11403-1/-2
 29.755 MPa
@Strain 1.50 %,
Temperature 100 °C		4315.6 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 11403-1/-2
 30.111 MPa
@Strain 0.900 %,
Temperature 60.0 °C		4367.2 psi
@Strain 0.900 %,
Temperature 140 °F		ISO 11403-1/-2
 30.118 MPa
@Strain 0.500 %,
Temperature 40.0 °C		4368.3 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 11403-1/-2
 30.233 MPa
@Strain 1.30 %,
Temperature 80.0 °C		4384.9 psi
@Strain 1.30 %,
Temperature 176 °F		ISO 11403-1/-2
 30.234 MPa
@Strain 0.500 %,
Temperature 23.0 °C		4385.1 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 11403-1/-2
 30.451 MPa
@Strain 1.80 %,
Temperature 120 °C		4416.6 psi
@Strain 1.80 %,
Temperature 248 °F		ISO 11403-1/-2
 30.725 MPa
@Strain 0.500 %,
Temperature 0.000 °C		4456.3 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 11403-1/-2
 31.169 MPa
@Strain 1.60 %,
Temperature 100 °C		4520.7 psi
@Strain 1.60 %,
Temperature 212 °F		ISO 11403-1/-2
 31.467 MPa
@Strain 1.90 %,
Temperature 120 °C		4563.9 psi
@Strain 1.90 %,
Temperature 248 °F		ISO 11403-1/-2
 31.929 MPa
@Strain 1.40 %,
Temperature 80.0 °C		4630.9 psi
@Strain 1.40 %,
Temperature 176 °F		ISO 11403-1/-2
 32.109 MPa
@Strain 0.500 %,
Temperature -40.0 °C		4657.0 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 11403-1/-2
 32.47 MPa
@Strain 1.70 %,
Temperature 100 °C		4709 psi
@Strain 1.70 %,
Temperature 212 °F		ISO 11403-1/-2
 32.52 MPa
@Strain 2.00 %,
Temperature 120 °C		4717 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 11403-1/-2
 32.792 MPa
@Strain 1.00 %,
Temperature 60.0 °C		4756.1 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 11403-1/-2
 33.442 MPa
@Strain 2.10 %,
Temperature 120 °C		4850.4 psi
@Strain 2.10 %,
Temperature 248 °F		ISO 11403-1/-2
 33.567 MPa
@Strain 1.50 %,
Temperature 80.0 °C		4868.5 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 11403-1/-2
 33.702 MPa
@Strain 1.80 %,
Temperature 100 °C		4888.1 psi
@Strain 1.80 %,
Temperature 212 °F		ISO 11403-1/-2
 34.386 MPa
@Strain 2.20 %,
Temperature 120 °C		4987.3 psi
@Strain 2.20 %,
Temperature 248 °F		ISO 11403-1/-2
 34.887 MPa
@Strain 1.90 %,
Temperature 100 °C		5059.9 psi
@Strain 1.90 %,
Temperature 212 °F		ISO 11403-1/-2
 34.957 MPa
@Strain 0.600 %,
Temperature 23.0 °C		5070.1 psi
@Strain 0.600 %,
Temperature 73.4 °F		ISO 11403-1/-2
 35.137 MPa
@Strain 1.60 %,
Temperature 80.0 °C		5096.2 psi
@Strain 1.60 %,
Temperature 176 °F		ISO 11403-1/-2
 35.216 MPa
@Strain 2.30 %,
Temperature 120 °C		5107.7 psi
@Strain 2.30 %,
Temperature 248 °F		ISO 11403-1/-2
 35.366 MPa
@Strain 1.10 %,
Temperature 60.0 °C		5129.4 psi
@Strain 1.10 %,
Temperature 140 °F		ISO 11403-1/-2
 36.017 MPa
@Strain 2.00 %,
Temperature 100 °C		5223.8 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 11403-1/-2
 36.056 MPa
@Strain 2.40 %,
Temperature 120 °C		5229.5 psi
@Strain 2.40 %,
Temperature 248 °F		ISO 11403-1/-2
 36.287 MPa
@Strain 0.600 %,
Temperature 40.0 °C		5263.0 psi
@Strain 0.600 %,
Temperature 104 °F		ISO 11403-1/-2
 36.588 MPa
@Strain 1.70 %,
Temperature 80.0 °C		5306.7 psi
@Strain 1.70 %,
Temperature 176 °F		ISO 11403-1/-2
 36.761 MPa
@Strain 0.600 %,
Temperature 0.000 °C		5331.7 psi
@Strain 0.600 %,
Temperature 32.0 °F		ISO 11403-1/-2
 36.789 MPa
@Strain 2.50 %,
Temperature 120 °C		5335.8 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 11403-1/-2
 37.123 MPa
@Strain 2.10 %,
Temperature 100 °C		5384.2 psi
@Strain 2.10 %,
Temperature 212 °F		ISO 11403-1/-2
 37.543 MPa
@Strain 2.60 %,
Temperature 120 °C		5445.2 psi
@Strain 2.60 %,
Temperature 248 °F		ISO 11403-1/-2
 37.712 MPa
@Strain 1.20 %,
Temperature 60.0 °C		5469.7 psi
@Strain 1.20 %,
Temperature 140 °F		ISO 11403-1/-2
 37.971 MPa
@Strain 1.80 %,
Temperature 80.0 °C		5507.2 psi
@Strain 1.80 %,
Temperature 176 °F		ISO 11403-1/-2
 38.122 MPa
@Strain 2.20 %,
Temperature 100 °C		5529.1 psi
@Strain 2.20 %,
Temperature 212 °F		ISO 11403-1/-2
 38.211 MPa
@Strain 2.70 %,
Temperature 120 °C		5542.0 psi
@Strain 2.70 %,
Temperature 248 °F		ISO 11403-1/-2
 38.306 MPa
@Strain 0.600 %,
Temperature -40.0 °C		5555.8 psi
@Strain 0.600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 38.874 MPa
@Strain 2.80 %,
Temperature 120 °C		5638.2 psi
@Strain 2.80 %,
Temperature 248 °F		ISO 11403-1/-2
 39.111 MPa
@Strain 2.30 %,
Temperature 100 °C		5672.6 psi
@Strain 2.30 %,
Temperature 212 °F		ISO 11403-1/-2
 39.291 MPa
@Strain 1.90 %,
Temperature 80.0 °C		5698.7 psi
@Strain 1.90 %,
Temperature 176 °F		ISO 11403-1/-2
 39.533 MPa
@Strain 2.90 %,
Temperature 120 °C		5733.8 psi
@Strain 2.90 %,
Temperature 248 °F		ISO 11403-1/-2
 39.785 MPa
@Strain 1.30 %,
Temperature 60.0 °C		5770.3 psi
@Strain 1.30 %,
Temperature 140 °F		ISO 11403-1/-2
 40.151 MPa
@Strain 3.00 %,
Temperature 120 °C		5823.4 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 11403-1/-2
 40.158 MPa
@Strain 2.40 %,
Temperature 100 °C		5824.4 psi
@Strain 2.40 %,
Temperature 212 °F		ISO 11403-1/-2
 40.716 MPa
@Strain 3.10 %,
Temperature 120 °C		5905.4 psi
@Strain 3.10 %,
Temperature 248 °F		ISO 11403-1/-2
 40.735 MPa
@Strain 2.00 %,
Temperature 80.0 °C		5908.1 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 11403-1/-2
 41.05 MPa
@Strain 2.50 %,
Temperature 100 °C		5954 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 11403-1/-2
 41.156 MPa
@Strain 0.700 %,
Temperature 40.0 °C		5969.2 psi
@Strain 0.700 %,
Temperature 104 °F		ISO 11403-1/-2
 41.2 MPa
@Strain 3.20 %,
Temperature 120 °C		5980 psi
@Strain 3.20 %,
Temperature 248 °F		ISO 11403-1/-2
 41.349 MPa
@Strain 0.700 %,
Temperature 23.0 °C		5997.2 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 41.687 MPa
@Strain 3.30 %,
Temperature 120 °C		6046.2 psi
@Strain 3.30 %,
Temperature 248 °F		ISO 11403-1/-2
 41.926 MPa
@Strain 2.60 %,
Temperature 100 °C		6080.9 psi
@Strain 2.60 %,
Temperature 212 °F		ISO 11403-1/-2
 42.023 MPa
@Strain 3.40 %,
Temperature 120 °C		6094.9 psi
@Strain 3.40 %,
Temperature 248 °F		ISO 11403-1/-2
 42.079 MPa
@Strain 2.10 %,
Temperature 80.0 °C		6103.1 psi
@Strain 2.10 %,
Temperature 176 °F		ISO 11403-1/-2
 42.105 MPa
@Strain 0.700 %,
Temperature 0.000 °C		6106.8 psi
@Strain 0.700 %,
Temperature 32.0 °F		ISO 11403-1/-2
 42.274 MPa
@Strain 1.40 %,
Temperature 60.0 °C		6131.3 psi
@Strain 1.40 %,
Temperature 140 °F		ISO 11403-1/-2
 42.703 MPa
@Strain 2.70 %,
Temperature 100 °C		6193.6 psi
@Strain 2.70 %,
Temperature 212 °F		ISO 11403-1/-2
 43.337 MPa
@Strain 2.20 %,
Temperature 80.0 °C		6285.5 psi
@Strain 2.20 %,
Temperature 176 °F		ISO 11403-1/-2
 43.522 MPa
@Strain 2.80 %,
Temperature 100 °C		6312.3 psi
@Strain 2.80 %,
Temperature 212 °F		ISO 11403-1/-2
 44.236 MPa
@Strain 2.90 %,
Temperature 100 °C		6415.9 psi
@Strain 2.90 %,
Temperature 212 °F		ISO 11403-1/-2
 44.463 MPa
@Strain 1.50 %,
Temperature 60.0 °C		6448.8 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 11403-1/-2
 44.496 MPa
@Strain 2.30 %,
Temperature 80.0 °C		6453.6 psi
@Strain 2.30 %,
Temperature 176 °F		ISO 11403-1/-2
 44.857 MPa
@Strain 0.700 %,
Temperature -40.0 °C		6506.0 psi
@Strain 0.700 %,
Temperature -40.0 °F		ISO 11403-1/-2
 44.953 MPa
@Strain 3.00 %,
Temperature 100 °C		6519.9 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 11403-1/-2
 45.557 MPa
@Strain 3.10 %,
Temperature 100 °C		6607.5 psi
@Strain 3.10 %,
Temperature 212 °F		ISO 11403-1/-2
 45.678 MPa
@Strain 2.40 %,
Temperature 80.0 °C		6625.0 psi
@Strain 2.40 %,
Temperature 176 °F		ISO 11403-1/-2
 46.192 MPa
@Strain 3.20 %,
Temperature 100 °C		6699.6 psi
@Strain 3.20 %,
Temperature 212 °F		ISO 11403-1/-2
 46.603 MPa
@Strain 1.60 %,
Temperature 60.0 °C		6759.2 psi
@Strain 1.60 %,
Temperature 140 °F		ISO 11403-1/-2
 46.749 MPa
@Strain 3.30 %,
Temperature 100 °C		6780.4 psi
@Strain 3.30 %,
Temperature 212 °F		ISO 11403-1/-2
 46.757 MPa
@Strain 2.50 %,
Temperature 80.0 °C		6781.5 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 11403-1/-2
 46.761 MPa
@Strain 0.800 %,
Temperature 40.0 °C		6782.1 psi
@Strain 0.800 %,
Temperature 104 °F		ISO 11403-1/-2
 47.026 MPa
@Strain 0.800 %,
Temperature 23.0 °C		6820.6 psi
@Strain 0.800 %,
Temperature 73.4 °F		ISO 11403-1/-2
 47.305 MPa
@Strain 3.40 %,
Temperature 100 °C		6861.0 psi
@Strain 3.40 %,
Temperature 212 °F		ISO 11403-1/-2
 47.769 MPa
@Strain 2.60 %,
Temperature 80.0 °C		6928.3 psi
@Strain 2.60 %,
Temperature 176 °F		ISO 11403-1/-2
 47.791 MPa
@Strain 3.50 %,
Temperature 100 °C		6931.5 psi
@Strain 3.50 %,
Temperature 212 °F		ISO 11403-1/-2
 48.11 MPa
@Strain 0.800 %,
Temperature 0.000 °C		6978 psi
@Strain 0.800 %,
Temperature 32.0 °F		ISO 11403-1/-2
 48.258 MPa
@Strain 3.60 %,
Temperature 100 °C		6999.2 psi
@Strain 3.60 %,
Temperature 212 °F		ISO 11403-1/-2
 48.652 MPa
@Strain 1.70 %,
Temperature 60.0 °C		7056.4 psi
@Strain 1.70 %,
Temperature 140 °F		ISO 11403-1/-2
 48.69 MPa
@Strain 3.70 %,
Temperature 100 °C		7062 psi
@Strain 3.70 %,
Temperature 212 °F		ISO 11403-1/-2
 48.722 MPa
@Strain 2.70 %,
Temperature 80.0 °C		7066.5 psi
@Strain 2.70 %,
Temperature 176 °F		ISO 11403-1/-2
 49.051 MPa
@Strain 3.80 %,
Temperature 100 °C		7114.3 psi
@Strain 3.80 %,
Temperature 212 °F		ISO 11403-1/-2
 49.451 MPa
@Strain 3.90 %,
Temperature 100 °C		7172.3 psi
@Strain 3.90 %,
Temperature 212 °F		ISO 11403-1/-2
 49.658 MPa
@Strain 2.80 %,
Temperature 80.0 °C		7202.3 psi
@Strain 2.80 %,
Temperature 176 °F		ISO 11403-1/-2
 49.759 MPa
@Strain 4.00 %,
Temperature 100 °C		7216.9 psi
@Strain 4.00 %,
Temperature 212 °F		ISO 11403-1/-2
 50.072 MPa
@Strain 4.10 %,
Temperature 100 °C		7262.3 psi
@Strain 4.10 %,
Temperature 212 °F		ISO 11403-1/-2
 50.275 MPa
@Strain 4.20 %,
Temperature 100 °C		7291.8 psi
@Strain 4.20 %,
Temperature 212 °F		ISO 11403-1/-2
 50.514 MPa
@Strain 2.90 %,
Temperature 80.0 °C		7326.4 psi
@Strain 2.90 %,
Temperature 176 °F		ISO 11403-1/-2
 50.546 MPa
@Strain 1.80 %,
Temperature 60.0 °C		7331.1 psi
@Strain 1.80 %,
Temperature 140 °F		ISO 11403-1/-2
 51.058 MPa
@Strain 0.800 %,
Temperature -40.0 °C		7405.3 psi
@Strain 0.800 %,
Temperature -40.0 °F		ISO 11403-1/-2
 51.338 MPa
@Strain 3.00 %,
Temperature 80.0 °C		7446.0 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 11403-1/-2
 52.059 MPa
@Strain 0.900 %,
Temperature 40.0 °C		7550.5 psi
@Strain 0.900 %,
Temperature 104 °F		ISO 11403-1/-2
 52.132 MPa
@Strain 3.10 %,
Temperature 80.0 °C		7561.1 psi
@Strain 3.10 %,
Temperature 176 °F		ISO 11403-1/-2
 52.317 MPa
@Strain 0.900 %,
Temperature 23.0 °C		7588.0 psi
@Strain 0.900 %,
Temperature 73.4 °F		ISO 11403-1/-2
 52.325 MPa
@Strain 1.90 %,
Temperature 60.0 °C		7589.1 psi
@Strain 1.90 %,
Temperature 140 °F		ISO 11403-1/-2
 52.84 MPa
@Strain 3.20 %,
Temperature 80.0 °C		7664 psi
@Strain 3.20 %,
Temperature 176 °F		ISO 11403-1/-2
 53.524 MPa
@Strain 3.30 %,
Temperature 80.0 °C		7763.0 psi
@Strain 3.30 %,
Temperature 176 °F		ISO 11403-1/-2
 53.681 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7785.8 psi
@Strain 0.900 %,
Temperature 32.0 °F		ISO 11403-1/-2
 54.067 MPa
@Strain 2.00 %,
Temperature 60.0 °C		7841.8 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 11403-1/-2
 54.146 MPa
@Strain 3.40 %,
Temperature 80.0 °C		7853.2 psi
@Strain 3.40 %,
Temperature 176 °F		ISO 11403-1/-2
 54.758 MPa
@Strain 3.50 %,
Temperature 80.0 °C		7942.0 psi
@Strain 3.50 %,
Temperature 176 °F		ISO 11403-1/-2
 55.316 MPa
@Strain 3.60 %,
Temperature 80.0 °C		8022.9 psi
@Strain 3.60 %,
Temperature 176 °F		ISO 11403-1/-2
 55.686 MPa
@Strain 2.10 %,
Temperature 60.0 °C		8076.6 psi
@Strain 2.10 %,
Temperature 140 °F		ISO 11403-1/-2
 55.854 MPa
@Strain 3.70 %,
Temperature 80.0 °C		8101.0 psi
@Strain 3.70 %,
Temperature 176 °F		ISO 11403-1/-2
 56.352 MPa
@Strain 3.80 %,
Temperature 80.0 °C		8173.2 psi
@Strain 3.80 %,
Temperature 176 °F		ISO 11403-1/-2
 56.802 MPa
@Strain 3.90 %,
Temperature 80.0 °C		8238.4 psi
@Strain 3.90 %,
Temperature 176 °F		ISO 11403-1/-2
 56.918 MPa
@Strain 1.00 %,
Temperature 40.0 °C		8255.3 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 11403-1/-2
 57.0 MPa
@Strain 1.00 %,
Temperature 23.0 °C		8270 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 57.071 MPa
@Strain 0.900 %,
Temperature -40.0 °C		8277.5 psi
@Strain 0.900 %,
Temperature -40.0 °F		ISO 11403-1/-2
 57.227 MPa
@Strain 2.20 %,
Temperature 60.0 °C		8300.1 psi
@Strain 2.20 %,
Temperature 140 °F		ISO 11403-1/-2
 57.233 MPa
@Strain 4.00 %,
Temperature 80.0 °C		8301.0 psi
@Strain 4.00 %,
Temperature 176 °F		ISO 11403-1/-2
 57.617 MPa
@Strain 4.10 %,
Temperature 80.0 °C		8356.7 psi
@Strain 4.10 %,
Temperature 176 °F		ISO 11403-1/-2
 57.998 MPa
@Strain 4.20 %,
Temperature 80.0 °C		8411.9 psi
@Strain 4.20 %,
Temperature 176 °F		ISO 11403-1/-2
 58.3 MPa
@Strain 4.30 %,
Temperature 80.0 °C		8460 psi
@Strain 4.30 %,
Temperature 176 °F		ISO 11403-1/-2
 58.647 MPa
@Strain 4.40 %,
Temperature 80.0 °C		8506.0 psi
@Strain 4.40 %,
Temperature 176 °F		ISO 11403-1/-2
 58.731 MPa
@Strain 2.30 %,
Temperature 60.0 °C		8518.2 psi
@Strain 2.30 %,
Temperature 140 °F		ISO 11403-1/-2
 58.899 MPa
@Strain 4.50 %,
Temperature 80.0 °C		8542.6 psi
@Strain 4.50 %,
Temperature 176 °F		ISO 11403-1/-2
 59.006 MPa
@Strain 1.00 %,
Temperature 0.000 °C		8558.1 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 59.125 MPa
@Strain 4.60 %,
Temperature 80.0 °C		8575.4 psi
@Strain 4.60 %,
Temperature 176 °F		ISO 11403-1/-2
 59.328 MPa
@Strain 4.70 %,
Temperature 80.0 °C		8604.8 psi
@Strain 4.70 %,
Temperature 176 °F		ISO 11403-1/-2
 59.476 MPa
@Strain 4.80 %,
Temperature 80.0 °C		8626.3 psi
@Strain 4.80 %,
Temperature 176 °F		ISO 11403-1/-2
 59.568 MPa
@Strain 5.00 %,
Temperature 80.0 °C		8639.6 psi
@Strain 5.00 %,
Temperature 176 °F		ISO 11403-1/-2
 59.627 MPa
@Strain 4.90 %,
Temperature 80.0 °C		8648.2 psi
@Strain 4.90 %,
Temperature 176 °F		ISO 11403-1/-2
 60.083 MPa
@Strain 2.40 %,
Temperature 60.0 °C		8714.3 psi
@Strain 2.40 %,
Temperature 140 °F		ISO 11403-1/-2
 61.451 MPa
@Strain 2.50 %,
Temperature 60.0 °C		8912.7 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 11403-1/-2
 61.503 MPa
@Strain 1.10 %,
Temperature 40.0 °C		8920.3 psi
@Strain 1.10 %,
Temperature 104 °F		ISO 11403-1/-2
 61.553 MPa
@Strain 1.10 %,
Temperature 23.0 °C		8927.5 psi
@Strain 1.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 62.728 MPa
@Strain 2.60 %,
Temperature 60.0 °C		9097.9 psi
@Strain 2.60 %,
Temperature 140 °F		ISO 11403-1/-2
 63.134 MPa
@Strain 1.00 %,
Temperature -40.0 °C		9156.8 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 63.919 MPa
@Strain 2.70 %,
Temperature 60.0 °C		9270.7 psi
@Strain 2.70 %,
Temperature 140 °F		ISO 11403-1/-2
 64.435 MPa
@Strain 1.10 %,
Temperature 0.000 °C		9345.5 psi
@Strain 1.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 65.086 MPa
@Strain 2.80 %,
Temperature 60.0 °C		9439.9 psi
@Strain 2.80 %,
Temperature 140 °F		ISO 11403-1/-2
 65.976 MPa
@Strain 1.20 %,
Temperature 40.0 °C		9569.0 psi
@Strain 1.20 %,
Temperature 104 °F		ISO 11403-1/-2
 66.124 MPa
@Strain 2.90 %,
Temperature 60.0 °C		9590.5 psi
@Strain 2.90 %,
Temperature 140 °F		ISO 11403-1/-2
 66.449 MPa
@Strain 1.20 %,
Temperature 23.0 °C		9637.6 psi
@Strain 1.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 67.119 MPa
@Strain 3.00 %,
Temperature 60.0 °C		9734.8 psi
@Strain 3.00 %,
Temperature 140 °F		ISO 11403-1/-2
 68.049 MPa
@Strain 3.10 %,
Temperature 60.0 °C		9869.7 psi
@Strain 3.10 %,
Temperature 140 °F		ISO 11403-1/-2
 68.9 MPa
@Strain 3.20 %,
Temperature 60.0 °C		9990 psi
@Strain 3.20 %,
Temperature 140 °F		ISO 11403-1/-2
 69.04 MPa
@Strain 1.10 %,
Temperature -40.0 °C		10010 psi
@Strain 1.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 69.684 MPa
@Strain 3.30 %,
Temperature 60.0 °C		10107 psi
@Strain 3.30 %,
Temperature 140 °F		ISO 11403-1/-2
 69.71 MPa
@Strain 1.20 %,
Temperature 0.000 °C		10110 psi
@Strain 1.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 70.223 MPa
@Strain 1.30 %,
Temperature 40.0 °C		10185 psi
@Strain 1.30 %,
Temperature 104 °F		ISO 11403-1/-2
 70.406 MPa
@Strain 3.40 %,
Temperature 60.0 °C		10212 psi
@Strain 3.40 %,
Temperature 140 °F		ISO 11403-1/-2
 71.065 MPa
@Strain 3.50 %,
Temperature 60.0 °C		10307 psi
@Strain 3.50 %,
Temperature 140 °F		ISO 11403-1/-2
 71.233 MPa
@Strain 1.30 %,
Temperature 23.0 °C		10331 psi
@Strain 1.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 71.636 MPa
@Strain 3.60 %,
Temperature 60.0 °C		10390 psi
@Strain 3.60 %,
Temperature 140 °F		ISO 11403-1/-2
 72.145 MPa
@Strain 3.70 %,
Temperature 60.0 °C		10464 psi
@Strain 3.70 %,
Temperature 140 °F		ISO 11403-1/-2
 72.626 MPa
@Strain 3.80 %,
Temperature 60.0 °C		10534 psi
@Strain 3.80 %,
Temperature 140 °F		ISO 11403-1/-2
 73.012 MPa
@Strain 3.90 %,
Temperature 60.0 °C		10590 psi
@Strain 3.90 %,
Temperature 140 °F		ISO 11403-1/-2
 73.401 MPa
@Strain 4.00 %,
Temperature 60.0 °C		10646 psi
@Strain 4.00 %,
Temperature 140 °F		ISO 11403-1/-2
 73.682 MPa
@Strain 4.10 %,
Temperature 60.0 °C		10687 psi
@Strain 4.10 %,
Temperature 140 °F		ISO 11403-1/-2
 73.985 MPa
@Strain 4.20 %,
Temperature 60.0 °C		10731 psi
@Strain 4.20 %,
Temperature 140 °F		ISO 11403-1/-2
 74.195 MPa
@Strain 4.30 %,
Temperature 60.0 °C		10761 psi
@Strain 4.30 %,
Temperature 140 °F		ISO 11403-1/-2
 74.25 MPa
@Strain 1.40 %,
Temperature 40.0 °C		10770 psi
@Strain 1.40 %,
Temperature 104 °F		ISO 11403-1/-2
 74.382 MPa
@Strain 4.40 %,
Temperature 60.0 °C		10788 psi
@Strain 4.40 %,
Temperature 140 °F		ISO 11403-1/-2
 74.557 MPa
@Strain 4.50 %,
Temperature 60.0 °C		10814 psi
@Strain 4.50 %,
Temperature 140 °F		ISO 11403-1/-2
 74.669 MPa
@Strain 4.60 %,
Temperature 60.0 °C		10830 psi
@Strain 4.60 %,
Temperature 140 °F		ISO 11403-1/-2
 74.753 MPa
@Strain 1.20 %,
Temperature -40.0 °C		10842 psi
@Strain 1.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 74.781 MPa
@Strain 1.30 %,
Temperature 0.000 °C		10846 psi
@Strain 1.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 74.801 MPa
@Strain 4.70 %,
Temperature 60.0 °C		10849 psi
@Strain 4.70 %,
Temperature 140 °F		ISO 11403-1/-2
 74.857 MPa
@Strain 4.80 %,
Temperature 60.0 °C		10857 psi
@Strain 4.80 %,
Temperature 140 °F		ISO 11403-1/-2
 74.893 MPa
@Strain 4.90 %,
Temperature 60.0 °C		10862 psi
@Strain 4.90 %,
Temperature 140 °F		ISO 11403-1/-2
 74.907 MPa
@Strain 5.00 %,
Temperature 60.0 °C		10864 psi
@Strain 5.00 %,
Temperature 140 °F		ISO 11403-1/-2
 75.912 MPa
@Strain 1.40 %,
Temperature 23.0 °C		11010 psi
@Strain 1.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 77.988 MPa
@Strain 1.50 %,
Temperature 40.0 °C		11311 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 11403-1/-2
 79.772 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11570 psi
@Strain 1.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 80.393 MPa
@Strain 1.50 %,
Temperature 23.0 °C		11660 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 80.407 MPa
@Strain 1.30 %,
Temperature -40.0 °C		11662 psi
@Strain 1.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 81.404 MPa
@Strain 1.60 %,
Temperature 40.0 °C		11807 psi
@Strain 1.60 %,
Temperature 104 °F		ISO 11403-1/-2
 84.558 MPa
@Strain 1.50 %,
Temperature 0.000 °C		12264 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 84.636 MPa
@Strain 1.70 %,
Temperature 40.0 °C		12275 psi
@Strain 1.70 %,
Temperature 104 °F		ISO 11403-1/-2
 84.755 MPa
@Strain 1.60 %,
Temperature 23.0 °C		12293 psi
@Strain 1.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 85.954 MPa
@Strain 1.40 %,
Temperature -40.0 °C		12467 psi
@Strain 1.40 %,
Temperature -40.0 °F		ISO 11403-1/-2
 87.55 MPa
@Strain 1.80 %,
Temperature 40.0 °C		12700 psi
@Strain 1.80 %,
Temperature 104 °F		ISO 11403-1/-2
 88.897 MPa
@Strain 1.70 %,
Temperature 23.0 °C		12893 psi
@Strain 1.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 89.327 MPa
@Strain 1.60 %,
Temperature 0.000 °C		12956 psi
@Strain 1.60 %,
Temperature 32.0 °F		ISO 11403-1/-2
 90.154 MPa
@Strain 1.90 %,
Temperature 40.0 °C		13076 psi
@Strain 1.90 %,
Temperature 104 °F		ISO 11403-1/-2
 91.465 MPa
@Strain 1.50 %,
Temperature -40.0 °C		13266 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 11403-1/-2
 92.505 MPa
@Strain 2.00 %,
Temperature 40.0 °C		13417 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 11403-1/-2
 92.809 MPa
@Strain 1.80 %,
Temperature 23.0 °C		13461 psi
@Strain 1.80 %,
Temperature 73.4 °F		ISO 11403-1/-2
 93.907 MPa
@Strain 1.70 %,
Temperature 0.000 °C		13620 psi
@Strain 1.70 %,
Temperature 32.0 °F		ISO 11403-1/-2
 94.648 MPa
@Strain 2.10 %,
Temperature 40.0 °C		13728 psi
@Strain 2.10 %,
Temperature 104 °F		ISO 11403-1/-2
 96.557 MPa
@Strain 1.90 %,
Temperature 23.0 °C		14004 psi
@Strain 1.90 %,
Temperature 73.4 °F		ISO 11403-1/-2
 96.633 MPa
@Strain 2.20 %,
Temperature 40.0 °C		14015 psi
@Strain 2.20 %,
Temperature 104 °F		ISO 11403-1/-2
 96.686 MPa
@Strain 1.60 %,
Temperature -40.0 °C		14023 psi
@Strain 1.60 %,
Temperature -40.0 °F		ISO 11403-1/-2
 98.256 MPa
@Strain 1.80 %,
Temperature 0.000 °C		14251 psi
@Strain 1.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 98.379 MPa
@Strain 2.30 %,
Temperature 40.0 °C		14269 psi
@Strain 2.30 %,
Temperature 104 °F		ISO 11403-1/-2
 99.901 MPa
@Strain 2.40 %,
Temperature 40.0 °C		14489 psi
@Strain 2.40 %,
Temperature 104 °F		ISO 11403-1/-2
 100.12 MPa
@Strain 2.00 %,
Temperature 23.0 °C		14521 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 101.33 MPa
@Strain 2.50 %,
Temperature 40.0 °C		14697 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 11403-1/-2
 102 MPa
@Strain 1.70 %,
Temperature -40.0 °C		14800 psi
@Strain 1.70 %,
Temperature -40.0 °F		ISO 11403-1/-2
 102.54 MPa
@Strain 2.60 %,
Temperature 40.0 °C		14872 psi
@Strain 2.60 %,
Temperature 104 °F		ISO 11403-1/-2
 102.57 MPa
@Strain 1.90 %,
Temperature 0.000 °C		14877 psi
@Strain 1.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
 103.44 MPa
@Strain 2.10 %,
Temperature 23.0 °C		15003 psi
@Strain 2.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 103.61 MPa
@Strain 2.70 %,
Temperature 40.0 °C		15027 psi
@Strain 2.70 %,
Temperature 104 °F		ISO 11403-1/-2
 104.47 MPa
@Strain 2.80 %,
Temperature 40.0 °C		15152 psi
@Strain 2.80 %,
Temperature 104 °F		ISO 11403-1/-2
 105.2 MPa
@Strain 2.90 %,
Temperature 40.0 °C		15260 psi
@Strain 2.90 %,
Temperature 104 °F		ISO 11403-1/-2
 105.72 MPa
@Strain 3.00 %,
Temperature 40.0 °C		15333 psi
@Strain 3.00 %,
Temperature 104 °F		ISO 11403-1/-2
 106.05 MPa
@Strain 3.10 %,
Temperature 40.0 °C		15381 psi
@Strain 3.10 %,
Temperature 104 °F		ISO 11403-1/-2
 106.23 MPa
@Strain 3.20 %,
Temperature 40.0 °C		15407 psi
@Strain 3.20 %,
Temperature 104 °F		ISO 11403-1/-2
 106.52 MPa
@Strain 2.20 %,
Temperature 23.0 °C		15449 psi
@Strain 2.20 %,
Temperature 73.4 °F		ISO 11403-1/-2
 106.76 MPa
@Strain 2.00 %,
Temperature 0.000 °C		15484 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 11403-1/-2
 107.08 MPa
@Strain 1.80 %,
Temperature -40.0 °C		15531 psi
@Strain 1.80 %,
Temperature -40.0 °F		ISO 11403-1/-2
 109.38 MPa
@Strain 2.30 %,
Temperature 23.0 °C		15864 psi
@Strain 2.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 110.66 MPa
@Strain 2.10 %,
Temperature 0.000 °C		16050 psi
@Strain 2.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 112.05 MPa
@Strain 2.40 %,
Temperature 23.0 °C		16252 psi
@Strain 2.40 %,
Temperature 73.4 °F		ISO 11403-1/-2
 112.19 MPa
@Strain 1.90 %,
Temperature -40.0 °C		16272 psi
@Strain 1.90 %,
Temperature -40.0 °F		ISO 11403-1/-2
 114.38 MPa
@Strain 2.20 %,
Temperature 0.000 °C		16589 psi
@Strain 2.20 %,
Temperature 32.0 °F		ISO 11403-1/-2
 114.53 MPa
@Strain 2.50 %,
Temperature 23.0 °C		16611 psi
@Strain 2.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 116.72 MPa
@Strain 2.60 %,
Temperature 23.0 °C		16929 psi
@Strain 2.60 %,
Temperature 73.4 °F		ISO 11403-1/-2
 117.06 MPa
@Strain 2.00 %,
Temperature -40.0 °C		16978 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 11403-1/-2
 117.92 MPa
@Strain 2.30 %,
Temperature 0.000 °C		17103 psi
@Strain 2.30 %,
Temperature 32.0 °F		ISO 11403-1/-2
 118.68 MPa
@Strain 2.70 %,
Temperature 23.0 °C		17213 psi
@Strain 2.70 %,
Temperature 73.4 °F		ISO 11403-1/-2
 120.29 MPa
@Strain 2.80 %,
Temperature 23.0 °C		17447 psi
@Strain 2.80 %,
Temperature 73.4 °F		ISO 11403-1/-2
 121.28 MPa
@Strain 2.40 %,
Temperature 0.000 °C		17590 psi
@Strain 2.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 121.89 MPa
@Strain 2.10 %,
Temperature -40.0 °C		17679 psi
@Strain 2.10 %,
Temperature -40.0 °F		ISO 11403-1/-2
 122 MPa
@Strain 2.90 %,
Temperature 23.0 °C		17700 psi
@Strain 2.90 %,
Temperature 73.4 °F		ISO 11403-1/-2
 124 MPa
@Strain 3.00 %,
Temperature 23.0 °C		18000 psi
@Strain 3.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 124.53 MPa
@Strain 2.50 %,
Temperature 0.000 °C		18062 psi
@Strain 2.50 %,
Temperature 32.0 °F		ISO 11403-1/-2
 124.73 MPa
@Strain 2.20 %,
Temperature -40.0 °C		18091 psi
@Strain 2.20 %,
Temperature -40.0 °F		ISO 11403-1/-2
 127.46 MPa
@Strain 2.60 %,
Temperature 0.000 °C		18487 psi
@Strain 2.60 %,
Temperature 32.0 °F		ISO 11403-1/-2
 130.15 MPa
@Strain 2.70 %,
Temperature 0.000 °C		18877 psi
@Strain 2.70 %,
Temperature 32.0 °F		ISO 11403-1/-2
 132.76 MPa
@Strain 2.80 %,
Temperature 0.000 °C		19255 psi
@Strain 2.80 %,
Temperature 32.0 °F		ISO 11403-1/-2
 134.27 MPa
@Strain 2.90 %,
Temperature 0.000 °C		19474 psi
@Strain 2.90 %,
Temperature 32.0 °F		ISO 11403-1/-2
Elongation at Break 3.0 %
@Temperature 23.0 °C		3.0 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 6.50 GPa
@Temperature 23.0 °C		943 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 190 MPa
@Temperature 23.0 °C		27600 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus 5.80 GPa
@Temperature 23.0 °C		841 ksi
@Temperature 73.4 °F		ISO 178
Charpy Impact Unnotched  2.50 J/cm²
@Temperature 23.0 °C		11.9 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 3.00 J/cm²
@Temperature -30.0 °C		14.3 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  0.550 J/cm²
@Temperature 23.0 °C		2.62 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 2.00e+16 ohm-cm
@Temperature 23.0 °C		2.00e+16 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.9
@Frequency 100 Hz,
Temperature 23.0 °C		3.9
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  27.0 kV/mm
@Thickness 2.00 mm,
Temperature 23.0 °C		686 kV/in
@Thickness 0.0787 in,
Temperature 73.4 °F		IEC 60243-1
 27.0 kV/mm
@Thickness 2.00 mm,
Temperature 90.0 °C		686 kV/in
@Thickness 0.0787 in,
Temperature 194 °F		IEC 60243-1
 36.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		914 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 36.0 kV/mm
@Thickness 1.00 mm,
Temperature 90.0 °C		914 kV/in
@Thickness 0.0394 in,
Temperature 194 °F		IEC 60243-1
Dissipation Factor  0.0015
@Frequency 100 Hz,
Temperature 23.0 °C		0.0015
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.0027
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0027
@Frequency 1000 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index 275 V
@Temperature 23.0 °C		275 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  74.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		41.1 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 89.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		49.4 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 132 µm/m-°C
@Temperature 55.0 - 160 °C		73.3 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 223 °C433 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C392 °FISO 75-1/-2
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
Oxygen Index 19 %19 %ISO 4589-1/-2
Glow Wire Test  700 °C
@Thickness 0.900 mm		1290 °F
@Thickness 0.0354 in		IEC 60695-2-12
 700 °C
@Thickness 3.00 mm		1290 °F
@Thickness 0.118 in		IEC 60695-2-12
 725 °C
@Thickness 0.900 mm		1340 °F
@Thickness 0.0354 in		Ignition; IEC 60695-2-13
 725 °C
@Thickness 3.00 mm		1340 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 227 °C441 °F10°C/min; ISO 11357-1/-3
 260 °C500 °FOptimum
 250 - 270 °C482 - 518 °F
Mold Temperature 80.0 - 110 °C176 - 230 °F
 100 °C212 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Gloss, High
 Moisture Absorption, Low
 Renewable Resource Content
 Stiffness, Good
 Strength, Good
 Warpage, Low
FillerGlass Fiber Reinforcement
FormsPellets
GenericPolytrimethylene Terephthalate (PTT)
Material StatusContact Supplier for Availability
Part Marking Code>PTT-GF15<ISO 11469
Polymer FamilyPolyester
Polymer TypePTT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Renewably Sourced Resins
Region Available - GlobalYes
Resin IdentificationPTT-GF15ISO 1043
RoHS ComplianceContact Manufacturer
UsesAutomotive Applications
 Consumer Applications
 General Purpose
 Industrial Applications
 Parts, Engineering
 Parts, Machine/Mechanical
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39712.html

免责声明: 本文 DuPont Performance Polymers Sorona® 3015G NC010 Polytrimethylene Terephthalate (PTT) 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4