- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 958 % | 958 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1190 % | 1190 % | ASTM D882 | ||
| Secant Modulus, MD | 0.175 GPa | 25.4 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.205 GPa | 29.7 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.70 | 0.70 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 14.6 g/micron | 371 g/mil | ASTM 1922 | ||
| Dart Drop | 2.55 g/micron | 64.8 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.8 % | 8.8 % | ASTM D1003 | ||
| Gloss | 10.7 % | 10.7 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock and PPA | ||||
| Minimum Recommended Thickness | 30 µm | ||||