- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 20.0 microns | 0.787 mil | |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 74.0 MPa | 10700 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 77.0 MPa | 11200 psi | ASTM D882 |
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 |
| Secant Modulus, MD | 0.110 GPa | 16.0 ksi | 1%; ASTM D882 |
| Secant Modulus, TD | 0.130 GPa | 18.9 ksi | 1%; ASTM D882 |
| Elmendorf Tear Strength, MD | 8.00 g/micron | 203 g/mil | ASTM 1922 |
| Elmendorf Tear Strength, TD | 23.0 g/micron | 584 g/mil | ASTM 1922 |
| Dart Drop | >= 7.20 g/micron | >= 183 g/mil | ASTM D1709 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 14 % | 14 % | ASTM D2457 |