- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.410
- 热变形温度 [℃]: 51.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| ESCR 100% Igepal® | >= 2000 hour | >= 2000 hour | ASTM D1693 | ||
| ESCR 10% Igepal® | >= 2000 hour | >= 2000 hour | ASTM D1693 | ||
| Oxidative Induction Time (OIT) | >= 100 min | >= 100 min | ASTM D3895 | ||
| Melt Index of Compound | 0.35 g/10 min | 0.35 g/10 min | Condition 190/2.16; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 51 | 51 | ASTM D2240 | ||
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | 2 in/min, Type IV bar; ASTM D638 | ||
| Elongation at Break | 700 % | 700 % | 2 in/min, Type IV bar; ASTM D638 | ||
| Flexural Modulus | 0.410 GPa | 59.5 ksi | ASTM D790 | ||
| Tensile Impact Strength | NB | NB | Type S bar; ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | ASTM D648 | ||
| Vicat Softening Point | 100 °C | 212 °F | Loading 1, Rate A; ASTM D1525 | ||
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A, type 1 specimen; ASTM D746 | ||
| Descriptive Properties | |||||
| SP-NCTL | Min 1000 | Single-point notched constant tensile load | |||