- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Condition E; ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 525 % | 525 % | ASTM D882 |
| Film Elongation at Break, TD | 675 % | 675 % | ASTM D882 |
| Secant Modulus, MD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.270 GPa | 39.2 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 5.91 g/micron | 150 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.6 g/micron | 575 g/mil | ASTM D1922 |
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F50; 1.5 in. dart/26 in. drop height; ASTM D 1709 |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D2457 |
| Gloss | 50 % | 50 % | at 45°. ASTM D 2457 |
| 90 % | 90 % | at 60°. ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 °C | 428 °F | |