- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Slip Level | 1200 ppm | 1200 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.76 MPa | 1705 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.64 MPa | 1834 psi | ASTM D882 |
| Film Elongation at Break, MD | 670 % | 670 % | ASTM D882 |
| Film Elongation at Break, TD | 771 % | 771 % | ASTM D882 |
| Secant Modulus, MD | 0.196094 GPa | 28.4414 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.234229 GPa | 33.9725 ksi | 2% Secant; ASTM D882 |
| Impact | 118 | 118 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 3295 | 3295 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 3528 | 3528 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 738 g | 738 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1170 g | 1170 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 14.5 g/micron | 369 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.0 g/micron | 585 g/mil | ASTM D1922 |
| Dart drop Test | 276 g | 0.609 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 51.93 MPa | 7532 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.3 MPa | 6420 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 67 % | 67 % | 45°; ASTM D2457 |