- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Antiblock Level | 5000 ppm | 5000 ppm | |
| Slip Level | 900 ppm | 900 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.4 MPa | 1650 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.51 MPa | 1525 psi | ASTM D882 |
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 |
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 475 g | 475 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 14.8 g/micron | 375 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.376 g/micron | 593.75 g/mil | ASTM D1922 |
| Dart drop Test | 400 g | 0.882 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 46.9 MPa | 6800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 42.7 MPa | 6200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | Dow Method (DSC) |