- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9215
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9215 g/cc | 0.03329 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 1000 ppm | 1000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.7 MPa | 1550 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.4 MPa | 1650 psi | ASTM D882 |
| Film Elongation at Break, MD | 437 % | 437 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Secant Modulus, MD | 0.183401 GPa | 26.6004 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.21098 GPa | 30.600 ksi | 2% Secant; ASTM D882 |
| Impact | 105 | 105 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 923 | 923 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 1086 | 1086 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 248 g | 248 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 689 g | 689 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 12.2 g/micron | 310 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.907 g/micron | 861.25 g/mil | ASTM D1922 |
| Dart drop Test | 153 g | 0.337 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 38.01 MPa | 5513 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 56 % | 56 % | 45°; ASTM D2457 |