- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9188
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9188 g/cc | 0.03319 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.37 MPa | 1794 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.98 MPa | 1882 psi | ASTM D882 |
| Film Elongation at Break, MD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Break, TD | 857 % | 857 % | ASTM D882 |
| Secant Modulus, MD | 0.196039 GPa | 28.4334 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.220729 GPa | 32.0145 ksi | 2% Secant; ASTM D882 |
| Impact | 12 | 12 | [lbf]; Puncture Resistance Force; Dow Method |
| 305 | 305 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3668 | 3668 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4268 | 4268 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 4.63 J | 3.42 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 374 g | 374 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 699 g | 699 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.41 g/micron | 467.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 34.400 g/micron | 873.75 g/mil | ASTM D1922 |
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B |
| 114 g | 0.251 lb | Method A; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 64.78 MPa | 9396 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 52.41 MPa | 7602 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 9.80 N | 2.20 lb (f) | at 130°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 110 °C | 230 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |
| 87 % | 87 % | 20°; ASTM D2457 | |