- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.9178
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9178 g/cc | 0.03316 lb/in³ | ASTM D792 | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.818 MPa | 1424 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.34 MPa | 1499 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 697 % | 697 % | ASTM D882 | ||
| Film Elongation at Break, TD | 797 % | 797 % | ASTM D882 | ||
| Elongation at Break | 471 % | 471 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.138074 GPa | 20.0263 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.137544 GPa | 19.9493 ksi | 2% Secant; ASTM D882 | ||
| Impact | 20 | 20 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 290 | 290 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| 2723 | 2723 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |||
| 3161 | 3161 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |||
| Puncture Energy | 8.81 J | 6.50 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 787 g | 787 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 1060 g | 1060 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 15.49 g/micron | 393.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 20.9 g/micron | 530 g/mil | ASTM D1922 | ||
| Dart drop Test | 206 g | 0.454 lb | Method B; ASTM D1709 | ||
| 332 g | 0.732 lb | Method A; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 38.36 MPa | 5564 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 37.54 MPa | 5445 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 91 % | 91 % | 45°; ASTM D2457 | ||
| 149 % | 149 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 311 | ASTM D5458, unstretched | |||