- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 6000 ppm | 6000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.09 MPa | 2334 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.50 MPa | 2393 psi | ASTM D882 |
| Film Elongation at Break, MD | 569 % | 569 % | ASTM D882 |
| Film Elongation at Break, TD | 842 % | 842 % | ASTM D882 |
| Secant Modulus, MD | 0.301632 GPa | 43.7487 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.326977 GPa | 47.4247 ksi | 2% Secant; ASTM D882 |
| Impact | 7.0 | 7.0 | [lbf]; Puncture Resistance Force; Dow Method |
| 101 | 101 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3622 | 3622 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4163 | 4163 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 1.47 J | 1.08 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 165 g | 165 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 801 g | 801 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.1201 g/micron | 206.25 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 39.4192 g/micron | 1001.25 g/mil | ASTM D1922 |
| Dart drop Test | 52.0 g | 0.115 lb | Method A; ASTM D1709 |
| <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 59.68 MPa | 8656 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.63 MPa | 6473 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 14.7 N | 3.30 lb (f) | at 160°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 18 % | 18 % | ASTM D1003 |
| Gloss | 23 % | 23 % | 20°; ASTM D2457 |
| 43 % | 43 % | 45°; ASTM D2457 | |