- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.9289
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9289 g/cc | 0.03356 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.22 MPa | 2352 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 16.14 MPa | 2341 psi | ASTM D882 |
| Film Elongation at Break, MD | 860 % | 860 % | ASTM D882 |
| Film Elongation at Break, TD | 817 % | 817 % | ASTM D882 |
| Secant Modulus, MD | 0.298453 GPa | 43.2877 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.262883 GPa | 38.1286 ksi | 2% Secant; ASTM D882 |
| Impact | 18 | 18 | [lbf]; Puncture Resistance Force; Dow Method |
| 118 | 118 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 4007 | 4007 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 4785 | 4785 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Puncture Energy | 4.63 J | 3.42 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 928 g | 928 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 1120 g | 1120 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.3 g/micron | 464 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.0 g/micron | 560 g/mil | ASTM D1922 |
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B; ASTM D1709 |
| 304 g | 0.670 lb | Method A; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 53.33 MPa | 7735 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 45.04 MPa | 6533 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 23.1 N | 5.19 lb (f) | at 160°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 73 % | 73 % | 45°; ASTM D2457 |
| 78 % | 78 % | 20°; ASTM D2457 | |