- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.230 GPa | 33.4 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.25 | <= 0.25 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.8 g/micron | 351 g/mil | ASTM D1922 |
| Dart Drop | 3.50 g/micron | 88.9 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.0 MPa | 3920 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % @Thickness 0.0250 mm | 12 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 195 - 220 °C | 383 - 428 °F | |