- 熔体流动速率 [g/10min]: 140.0
- 密度 [g/cm3]: 0.933
- 热变形温度 [℃]: 56.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Melt Flow | 140 g/10 min | 140 g/10 min | ASTM D1238 |
| Spiral Flow | 67.8 cm | 26.7 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2"/min; ASTM D638 |
| 1% Secant Modulus | 689 MPa | 100000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 0.593 GPa | 86.0 ksi | 0.5"/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |