- 熔体流动速率 [g/10min]: 6.6
- 密度 [g/cm3]: 0.91
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 6.6 g/10 min | 6.6 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.0760 GPa | 11.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0760 GPa | 11.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 530 g | 530 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 13.8 g/micron | 350 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 20.9 g/micron | 530 g/mil | ASTM D1922 |
| Dart Drop | 8.19 g/micron | 208 g/mil | ASTM D1709 |
| Dart drop Test | 208 g | 0.459 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 50 % | 50 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |