- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.124 GPa | 18.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.145 GPa | 21.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 480 g | 480 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 740 g | 740 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.9 g/micron | 480 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 29.1 g/micron | 740 g/mil | ASTM D1922 |
| Dart Drop | 4.88 g/micron | 124 g/mil | ASTM D1709 |
| Dart drop Test | 124 g | 0.273 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | >= 18.0 MPa | >= 2610 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.70 % | 0.70 % | ASTM D1003 |
| Gloss | 95 % | 95 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |