- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.138 GPa | 20.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 360 g | 360 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 720 g | 720 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 14.2 g/micron | 360 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.3 g/micron | 720 g/mil | ASTM D1922 |
| Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
| Dart drop Test | 200 g | 0.441 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.0 MPa | 5220 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | >= 19.0 MPa | >= 2760 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 60 % | 60 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 - 245 °C | 401 - 473 °F | |