- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 21.0
- 弯曲强度 [MPa]: 13.0
- 弯曲模量 [MPa]: 0.655
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Ultimate | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 670 % | 670 % | ASTM D638 |
| Modulus of Elasticity | 0.786 GPa | 114 ksi | ASTM D638 |
| Flexural Modulus | 0.655 GPa | 95.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |