- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 |
| Film Elongation at Break, TD | 870 % | 870 % | ASTM D882 |
| Secant Modulus, MD | 0.248 GPa | 36.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.324 GPa | 47.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 270 g | 270 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 660 g | 660 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 10.6 g/micron | 270 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 5.28 g/micron | 134 g/mil | ASTM D1709 |
| Dart drop Test | 134 g | 0.295 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 53.0 MPa | 7690 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 45.0 MPa | 6530 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 - 245 °C | 401 - 473 °F | |