- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 20.0 microns | 0.787 mil | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.52 MPa | 1090 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.03 MPa | 1020 psi | ASTM D882 |
| Film Elongation at Yield, MD | 470 % | 470 % | ASTM D638 |
| Film Elongation at Yield, TD | 780 % | 780 % | ASTM D882 |
| Elongation at Break | 360 % | 360 % | |
| Puncture Energy | 1.66 J | 1.22 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 375 g | 375 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 535 g | 535 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| 1% Secant Modulus, MD | 100 MPa | 14500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 120 MPa | 17400 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.80 % | 0.80 % | ASTM D1003 |
| Gloss | 85 % | 85 % | at 45°; ASTM D2457 |